ADDITION OF NATURAL POZZOLANA (DIATOMITE) TO IMPROVE RESISTANCE IN STRUCTURAL MORTAR
Keywords:
Pozzolan, Diatomite, Resistance, Mortar, StructuralAbstract
The investigative work carried out consisted in the evaluation of type (M) structural mortars, according to the standard (ASTM C109/C109 M-99), depending on the compressive strength. The tests were carried out with specific materials such as: Type I Portland cement, diatomite Pozzolana, crushed sand from (Megarok S.A.) and water. The mixtures were worked at the same fluidity level, obtaining homogeneous mixtures with great workability. The molding of the specimens was carried out in cubes of 50mm on each side. Diatomite was added proportionally at 15% and 20% as a replacement for Portland cement. Breakage tests were performed at 7, 14, 28, and 91 days of curing, which were successful, creating a type M (structural) mortar. The diatomite was very efficient thanks to its high amorphous silica content, which reacts with the hydration products of the cement ( and the alkalis and among others) to produce a structural mortar in order to obtain the required level of resistance and improve its durability.
Keywords: Pozzolan, Diatomite, Resistance, Mortar, Structural.
Downloads
References
Alcívar Véliz, M. L., & Loor Cobeña, H. P. (2022). La diatomita como adición mineral a un mortero de cemento portland. tabla 3. Análisis Químico de la diatomita.
ASTM C109/C109 M-99. (s.f.). Standard Test Method for Compressive Strenght of Hydraulic Cement Mortars.
ASTM, C618-01. (s.f.). Standard Spedification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for as a Mineral Admixture in Concrete. C 618-01. ASTM.
Cesar, M. (2022). Agregado fino densidad y absorcion de agua. Portoviejo: Laboratorio tecnico Megarok.
Holcim Ecuador S.A. (2022). Cemento hidráulico para pozo petrolero Clase G - HSR. Guayaquil.
INEN, NTE 1504. (1987). Cemento Hidraulicos. Aditivos De Porceso. Requisitos, NTE 1504, 1987. Quito: Instituto Ecuatoriano De Normalización. Obtenido de https://www.normalizacion.gob.ec/buzon/normas/nte_inen_1504.pdf
INEN, NTE 151. (2010). Cemento Hidráulico. Definición De Términos. NTE 151: 2010. Quito: Instituto Ecuatoriano De Normalización. Obtenido de https://www.normalizacion.gob.ec/buzon/normas/151.pdf
INEN, NTE 152. (2010). Cemento Portaln. Requisitos. NTE 152: 2010, Cuarta revisión. Quito: Instituto Ecuatoriano de normalización. Obtenido de https://www.normalizacion.gob.ec/buzon/normas/152.pdf
INEN, NTE 155. (2009). Cemento Hidráulico. Mezclado Mecánico De Pastas y Morteros De Consistencia Plástica. NTE 155: 2009. Quito: Instituto Ecuatoriano De Normalización. Obtenido de https://www.normalizacion.gob.ec/buzon/normas/155.pdf
INEN, NTE 1806. (2015). Cemento Para Mampostería. Requisitos. NTE 1806. INEN. Obtenido de https://www.normalizacion.gob.ec/buzon/normas/nte_inen_1806.pdf
INEN, NTE 2502. (2009-08). Cemento Hidraúlico. Determinación del Flujo En Morteros. NTE 2502: 2009. Quito: Instituto Ecuatoriana De Normalización. Obtenido de https://www.normalizacion.gob.ec/buzon/normas/nte_inen_2502.pdf
INEN, NTE 2518. (2010). Morteros para unidades de mamposteria requisitos NTE INEN 2 518:2010. Quito: Instituto Ecuatoriano de Normalización. Obtenido de https://www.normalizacion.gob.ec/buzon/normas/2518.pdf
INEN, NTE 2518. (2010). Morteros para unidades de mamposteria requisitos. NTE 2 518: 2010. INSTITUTO ECUATORIANO DE NORMALIZACIÓN. Obtenido de https://www.normalizacion.gob.ec/buzon/normas/2518.pdf
INEN, NTE 488. (2009). Cemento hidraúlico. Determinación de la resistencia a la compresión de morteros en cubos de 50 mm de arista. NTE 488: 2009. Quito: Instituto Ecuatoriano De Normalización. Obtenido de https://www.normalizacion.gob.ec/buzon/normas/488.pdf
INEN, NTE 488. (2009, julio). NTE INEN 488: 2009, Segunda revisión. Quito: Instituto ecuatoriano de normalización.
INEN, NTE 490. (2011). Cementos Hidráulicos compuesto. Requisitos. NTE 490: 2011. Quito: Instituto ecuatoriano de normalización. Obtenido de https://www.normalizacion.gob.ec/buzon/normas/490.pdf
INEN, NTE 696. (2010). Áridos. Análisis Granulométrico En Los Áridos, Fino y Grueso. NTE 696: 2010. Quito: Instituto Ecuatoriano De Normalización. Obtenido de https://www.normalizacion.gob.ec/buzon/normas/696.pdf
INEN, NTE 856. (2010). Áridos. Determinación De La Densidad, Densidad Relativa (Gravedad Específica) y Absorción del Árido Fino. NTE 856: 2010. Quito: Instituto Ecuatoriano De Normalización. Obtenido de https://www.normalizacion.gob.ec/buzon/normas/NTE_INEN_856.pdf
INEN, NTE 862. (2011). Áridos Para Hormigón. Determinación Del Contenido Total De Humedad. NTE 862: 2011. Quito: Instituto Ecuatoriano de Normalización. Obtenido de https://www.normalizacion.gob.ec/buzon/normas/862.pdf
INEN, NTE 872. (2011). Áridos Para Hormigón. Requisitos. NTE 872: 2011. Quito: Instituto Ecuatoriano De Normalización. Obtenido de https://www.normalizacion.gob.ec/buzon/normas/872-1.pdf
INEN, NTE 957. (2012). Cmento hidraúlico. Determinación de la finura mediante el tamiz de 45 μm No. 325. NTE 957: 2012. Quito: Instituto Ecuatoriano De Normalización. Obtenido de https://www.normalizacion.gob.ec/buzon/normas/nte_inen_957-3.pdf
Megarok S.A. (22 de Febrero de 2015). Megarok.com.ec. Obtenido de https://megarok.com.ec/web/portfolio-item/arena-homogenizada/
NTE INEN 488. (2009). STANDARD TEST METHOD FOR COMPRESSIVE STRENGTH OF HYDRAULIC CEMENT MORTARS (USING 50 – mm CUBE.
Valdiviezo A, R. J. (2009). En Geología Económica (pág. 141). Perú: INGEMMET.
Published
How to Cite
Issue
Section
License
Copyright (c) 2023 Scientific Journal INGENIAR: Engineering, Technology and Research
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.